Pengaruh Pengurangan Air dan Penambahan Superplasticizer terhadap Kuat Tarik, Geser, dan Lentur Pada Kuat Tekan Beton 15 MPa dan 20 MPa

Abstract

Berdasarkan komposisi campurannya, beton normal masih mungkin untuk ditmgkatkan lagi kinerjanya dengan mengurangkan kandungan air dan menambah superplasticizer. Kinerja yang dapat ditmgkatkan adalah kelecakan dan kuat tekannya. Pengurangan kandungan air dengan interval 0-30% dari kondisi normal dengan mempertahankan slump antara 150 - 180 mm tanpa terjadi bleeding dan segregation. Mutu beton yang direncanakan 15 dan 20 MPa yang diuji pada umur 28 hari. Hasil penelitian memperlihatkan bahwa pengurangan air dan penambahan superplasticizer, nilai slump antara 150 - 180 mm dapat tercapai tanpa terjadi bleeding dan scgregasi. Kuat Tank optimum sebesar 3,8667 MPa dan 4,6379 MPa untuk kuat lekan rencana 15 Mpa dan 20 MPa diperoleh pada pengurangan kandungan air 20% dan penambahan superplasticizer 1,91% dan 1,95% dan berat semen. Kuat geser optimum untuk kuat tekan rencana 15 MPa dan 20 MPa sebesar 6,2247 MPa dan 6,8644 MPa diperoleh pada pengurangan kandungan air 20% dan 25%, serta penambahan superplasticizer 1,91%, dan 2,05% dari berat semen. Kuat Letur optimum untuk kuat tekan rencana 15 MPa dan 20 MPa sebesar 4,9484 MPa dan 4,9106 MPa diperoleh pada pengurangan kandungan air 20% dan 25% serta penambahan superplasticizer 1,91% dan 2.05% dari berat semen. Keccpatan penctras, terkecil pada beton dengan kuat lekan rencana 15 MPa dan 20 MPa sebesar 0004 ? mmdtk pada pengurangan air 20%, (15 MPa) dan 25%, (20 MPa)'serta penambahan superplasticizer 1,91%, dan 2,05%, dan berat semen.

Based on its mixture composition, it's still possible for normal concrete to increase its performance by reducing the water content and adding superplasticizer. Performances can be increased is the workability and the compressive strength. Reduction ofwater content in range of 0-30% from normal condition is done by maintaining slump between 150-180 mm, without happened hv the bleeding and segregation. Compressive strength concrete planned is 15 and 20 MPa which is tested m age of 28 days. Result of research shows that reduction ofwater and addition of superplasticizer, slump vulue between 150-180 mm can be reached without bleeding and segregation. Optimum tensile strength at 3,8667 MPa and 4,6379 MPa for planned compressive strength 15 Mpa and 20 MPa obtained hv reduction the water content 20% and addition of superplasticizer 1,91% and 1,95%, of cement weight. Optimum shear strength for planned compressive strength 15 Mpa and 20 MPa of equal to 6,2247 MPa and 6,8644 MPa obtained by reduction the water content 20% and 25%, and also addition of superplasticizer 1,91%, and 2,05%, of cement weight. Optimum fle.xural strength forplanned compressive strength 15 Mpa and20 MPa ofequal to 4,94*4 MPaand 4.9/U6 MPa obtained byreduction the water content 20%, and 25%, and also addition <d superplasticizer 1,91%, and 2,05% of cement weight. Smallest penetrating speed <>t water at concrete for planned compressive strength /.•> Mpa and 20 MPa at i>.l>n42 nun dlk of reduction the water content 20'%, (15 MPa) and 25"" !2<> MPai and also addition ofsuperplasticizer 1,91%, and 2,95'%, of cement weight. A'<t vnnP warkiibilnv sunemlasiicizer tensile strength, shear strength, fle.xun'/ strength, permeability